The effects of current density and amount of discharge on dendrite formation in the lithium powder anode electrode
作者: Il Won SeongChang Hyun HongBok Ki KimWoo Young Yoon
作者单位: 1Division of Material Science Engineering, Korea University, 1, 5 Ga, Anam-dong, Sungbuk-ku, Seoul 136-701, Republic of Korea
2Department of Electronic Engineering, Kwangwoon University, 1, 447-Ga, Wolgye-dong, Nowon-ku, Seoul 137-701, Republic of Korea
刊名: Journal of Power Sources, 2007, Vol.178 (2), pp.769-773
来源数据库: Elsevier Journal
DOI: 10.1016/j.jpowsour.2007.12.062
关键词: Lithium secondary batteryLithium metal batteryLithium powder electrodeDendrite formation
原始语种摘要: Abstract(#br)A compacted lithium powder anode was used to improve the demerits of dendrite formation of lithium metal. Dendrite formation of lithium metal was restrained to use compacted lithium powder anode under a specific amount of discharge and the current density. In this study, the amount of discharge and the current density which suppress dendrite formation at the surface of a lithium powder electrode were investigated on an experimental basis. Discharge/charge reactions were accomplished on various values of the amount of discharge and current density by using beaker cells. It was analyzed by SEM images whether dendrite was formed or not on the surface of lithium powder electrode. From the various experiments, the relationship between current density and total amount of discharge...