Kinetics of Dispersion of the Molybdenum Nanofilms Deposited on Oxide Materials During Annealing in Vacuum
作者: Yu. V. Naidich, І. І. Gab, Т. V. Stetsyuk, B. D. Kоstyuk, D. B. Shakhnin
作者单位: 1I. M. Frantsevich Institute for Problems in Materials Science, NAS of Ukraine, 3 Academician Krzhyzhanovsky Str., UA-03142 Kyiv, Ukraine
2Open International University of Human Development ‘Ukraine’, 23 Lvivska Str., UA-03115 Kyiv, Ukraine
刊名: Metallofiz. Noveishie Tekhnol., 2018, Vol.40 (10), pp.1359-1373
来源数据库: G.V. Kurdyumov Institute for Metal Physics, National Academy of Science of the Ukraine
DOI: 10.15407/mfint.40.10.1359
关键词: Kinetics of dispersionMolybdenum nanofilmsLeucosapphireAlumina ceramicsSilicon glass.
原始语种摘要: The dispersion kinetics of molybdenum nanofilms of 100 nm thickness deposited on the leucosapphire, alumina ceramics or quartz glass substrates and annealed in vacuum at 1200–1600°C for different exposure times at each temperature in the interval of 2–20 min. As determined, the molybdenum film deposited on alumina ceramic is the most stable during annealing, and the least stable one is a film on quartz glass, which begins to intensively disperse and interact with the substrate surface above 1300°C. Based on the results of the investigations, the kinetic curves of films’ dispersion because of annealing are plotted.
全文获取路径: PDF下载  N.A.S. of Ukraine  (合作)
分享到:

×
关键词翻译
关键词翻译
  • alumina 矾土
  • Annealing 退火
  • molybdenum 
  • vacuum 真空
  • ceramics 陶瓷
  • thickness 厚度
  • glass 玻璃
  • annealing 热处理
  • stable 稳定的
  • annealed 已退火的