Properties of polyamide 6,10/poly(vinyl alcohol) blends and impact on oxygen barrier performance
作者: Jia‐wei WuYa‐qiong HuangHong‐bo LiJames RuntJen‐taut Yeh
作者单位: 1Key Laboratory for the Green Preparation and Application of Functional Materials, Faculty of Materials Science and Engineering Hubei University Wuhan China
2 Department of Materials Science and Engineering Penn State University, University Park Pennsylvania USA
3 Department of Materials Engineering Kun Shan University Tainan Taiwan
刊名: Polymer International, 2018, Vol.67 (4), pp.453-462
来源数据库: Wiley Journal
DOI: 10.1002/pi.5528
关键词: Nylon 610Poly(vinyl alcohol)Oxygen barrierFree volumeMiscibility
原始语种摘要: Abstract(#br)The oxygen transmission rate, average volume of free‐volume cavities ( V f) and fractional free volume ( F v) of polyamide 6,10 (PA610)/poly(vinyl alcohol) (PVA) (i.e. PA610 x PVA05 y , PA610 x PVA08 y and PA610 x PVA14 y ) blend films reduced to minimum values when their PVA contents reached corresponding optimal values. Oxygen transmission rate, V f and F v values obtained for optimal PA610 x PVA z y blown films were reduced considerably with decreasing PVA degrees of polymerization. The oxygen transmission rate of the optimal bio‐based PA61080PVA0520 blown film was...
全文获取路径: Wiley  (合作)
分享到:
来源刊物:

×
关键词翻译
关键词翻译
  • vinyl 乙烯基
  • polyamide 聚酰胺
  • barrier 堡坝
  • alcohol 
  • oxygen 
  • corresponding 对应的
  • diffraction 衍射
  • transmission 传送
  • attributed 属性
  • polymerization 聚合酌