Woven Fabric Carbon Fibre Composites Hybrid Joints under Quasi-Static Testing
作者: S.Y. Lee H. Ahmad
刊名: Journal of Advanced Manufacturing Technology, 2018, Vol.12 (1)
来源数据库: Penerbit Universiti Teknikal Malaysia Melaka
关键词: Hybrid JointsWoven FabricCFRPFailure ModesBearing Stress
原始语种摘要: Twill weave carbon fibre reinforced polymer (CFRP) hybrid adhesively bonded-bolted joints was investigated on bearing stress at failure in experimental programmes. The present paper comprises effects of joint type, normalised coupon width (W/d), laminate orientations and bolt load as specified in designed series. All CFRP hybrid joints exhibited cohesive failure before ultimate failure i.e., net-tension and bearing/net-tension failures. Bearing stress at failure was found to increase with normalized W/d and small W/d led to net-tension failure occurrence. Double-lap joints (DLJs) were stronger than single-lap joints (SLJs) due to secondary bending phenomenon in SLJs. Cross-ply presented greater strength than quasi-isotropic lay-up caused by the presence of 0˚ fibres orientation. Clamped...
全文获取路径: PDF下载  马六甲马来西亚技术大学  (合作)
分享到:

×
关键词翻译
关键词翻译
  • occur 产生
  • joints 纲线的交织
  • CFRP Carbon Fiber Reinforced Plastic
  • condition 条件
  • tension 张力
  • greater 较大
  • increase 增加
  • polymer 聚合物
  • applied 应用的
  • Testing 检测