Comparison of methanol/hydrochloric, ferric chloride acid versus tribochemical silica coating for adhesion of resin cement to zirconium dioxide
作者: Rodrigo Furtado de CarvalhoMutlu ÖzcanFrederico LouzadaEvelyn MonteiroMarco Antonio BottinoRenata Marques de MeloLuiz Felipe Valandro
作者单位: 1Department of Dentistry, Federal University of Juiz de Fora (UFJF)
2Dental Materials Unit, Center for Dental and Oral Medicine, Clinic for Fixed and Removable Prosthodontics and Dental Materials Science
3Dental School, Science and Technology Institute, São Paulo State University (UNESP)
4Department of Restorative Dentistry, Federal University of Santa Maria (UFSM), Division of Prosthodontics
刊名: Journal of Adhesion Science and Technology, 2016, Vol.30 (24), pp.2690-2698
来源数据库: Taylor & Francis Journal
DOI: 10.1080/01694243.2016.1197090
关键词: Adhesionair-abrasioncementationceramicsetchingmicroshear bond testsurface conditioningzirconia
原始语种摘要: AbstractThis study compared air-abrasion and etching regimens on adhesion of resin luting agent to zirconium dioxide. Ceramic specimens (LAVA, 3 M ESPE) (N = 16) were embedded in acrylic resin and exposed surfaces were polished. The specimens were randomly assigned into four groups (n = 12, 3 specimens for each disc): SC: Air-borne particle abrasion (30 μm aluminum oxide particles coated with silica, CoJet, 3 M ESPE); MH: Heated chemical solution (Methanol-800 mL; 37% Hydrochloric Acid-200 mL; Ferric Chloride-2 g) at 100 °C for 30 min, MHP: Primer (Metal/Zirconia Primer, Ivoclar Vivadent) + MH, P: Primer only (Metal/Zirconia Primer). Cylindrical molds (internal diameter: 0.7 mm; height: 1.5 mm) were placed on each conditioned specimen, filled with resin cement (Multilink Automix) and...
全文获取路径: Taylor & Francis  (合作)
分享到:
来源刊物:
影响因子:0.9 (2012)

×
关键词翻译
关键词翻译
  • resin 
  • silica 硅土
  • zirconium 
  • cement 胶结物
  • abrasion 海蚀
  • polymerized 聚合的
  • dioxide 二氧化物
  • adhesion 粘附
  • molds 霉菌
  • diameter 直径