Sodium Alginate-Based Ionic Conducting Membranes
作者: Y. O. IwakiM. Hernandez EscalonaJ. R. BrionesA. Pawlicka
作者单位: 1Instituto de Química de São Carlos , Universidade de São Paulo , Av. Trabalhador Sãocarlense 400, 13566-590 , São Carlos , SP , Brazil
2Centro de Biomateriales , Universidad de La Habana , Universidad s/n, e/G y Ronda, C. Habana 10600, A. P. 6130 , Cuba
3Facultad de Química , Universidad de La Habana , Calle Zapata s/n, e/G y Carlitos Aguirre , C. Habana , 10400 , Cuba
刊名: Molecular Crystals and Liquid Crystals, 2012, Vol.554 (1), pp.221-231
来源数据库: Taylor & Francis Journal
DOI: 10.1080/15421406.2012.634329
关键词: Acetic acidgel polymer electrolytelithium perchloratesodium alginate
原始语种摘要: The present study investigates gel polymer electrolytes (GPEs) based on sodium alginate plasticized with glycerol containing either CH3COOH or LiClO4. The membranes showed ionic conductivity results of 3.1 × 10−4 S/cm for the samples with LiClO4 and 8.7 × 10−5 S/cm for the samples with CH3COOH at room temperature. The samples also showed thermal stability up to 160°C, transparency of up to 90%, surface uniformity and adhesion to glass and steel. Moreover, Dynamic Mechanical Analysis revealed two relaxations for both samples and the Ea values were between 18 and 36 kJ/mol. All the results obtained indicate that alginate-based GPEs can be used as electrolytes in electrochemical devices.