Synthesis A Flexible Conductive Film of Poly 3,4-Ethylenedioxythiophene Polystyrene Sulfonate (PEDOT: PSS) Using Spray Pyrolysis Method
作者: Fadhil Muhammad TarmidziSetia Budi Sasongko
作者单位: 1Department of Chemical Engineering, Faculty of Engineering, Universitas Diponegoro, Indonesia
刊名: International Journal of Renewable Energy Development, 2018, Vol.7 (2), pp.159-162
来源数据库: Center of Biomass and Renewable Energy, Diponegoro University
DOI: 10.14710/ijred.7.2.159-162
关键词: PEDOT:PSSPETConductive polymerSpray pyrolysisFlexible film
原始语种摘要: Popularity of conducting polymers are become widely known and researches for practical application also has been done. In order to developed a continuous process for industrial scale, we have proposed a spray pyrolysis method to synthesis a flexible conductive film of Poly(3,4-ethylenedioxythiophene) poly(styrene sulfonate) (PEDOT:PSS) on poly(ethylene terephthalate) (PET) and annealed at different temperatures and spray distances. The optimum condition that resulting a best morphology was anneal at 90 o C and 20 cm distance with electrical conductivity 4.5 S/cm. It was found that annealing at temperature higher than 90 o C will resulting a stress to a film and formed crack due to a different thermal expansion, while at the distance higher than 20 cm resulting a loss of PEDOT:PSS...
全文获取路径: PDF下载  IJRED 
分享到:

×
关键词翻译
关键词翻译
  • 形态学 传导率
  • PSS Passenger Services System
  • resulting 引起的
  • annealed 已退火的
  • spray 喷雾
  • pyrolysis 加热分解
  • thickness 厚度
  • conductivity 传导率
  • morphology 传导率
  • styrene 苯乙烯
  • conductive 导电的