Preparation and Characterization of Polypropylene and Unsaturated Polyester Resin Filled with Jute Fiber
作者: Kamrun N. KeyaNasrin A. KonaMd. Sahadat HossainMd. RazzakMd. Naimul IslamRuhul A. Khan
作者单位: 1Institute of Radiation and Polymer Technology
刊名: Advanced Materials Research, 2020, Vol.4629 , pp.60-68
来源数据库: Trans Tech Journal
DOI: 10.4028/www.scientific.net/AMR.1156.60
关键词: Compression MoldingUnsaturated Polyester ResinJute FiberHand Lay-UpPolypropyleneMechanical Properties
原始语种摘要: Jute fabrics reinforced Polypropylene (PP) matrix composite was fabricated by compression molding and Unsaturated Polyester Resin (UPR) matrix composites were also fabricated by hand lay-up technique. The fiber content of the composites was 40% by weight. Mechanical properties between two types of composites were compared. Tensile Strength (TS), Tensile Modulus (TM), Elongation at break (Eb%) , and Impact Strength (IS) of the jute fabrics/PP composites were found to be 47 MPa, 1.2 GPa, 13% and 8 kg/cm, respectively. On the other hand, TS, TM, Eb%, and IS of the jute fabrics/UPR composite were found to be 43 MPa, 1.3 GPa, 10% and 6 kg/cm, respectively. It was found that both composites showed almost similar mechanical properties. After tensile testing, fracture sides of both types of the...
全文获取路径: PDF下载  Trans Tech 
分享到:

×
关键词翻译
关键词翻译
  • fabrics 纤维
  • composites 菊科植物
  • fabricated 制造
  • mechanical 机械的
  • properties 道具
  • reinforced 加筋的
  • UPR 
  • tensile 拉的
  • molding 浇铸
  • fiber 纤维