Influence of Cooling Time t<sub>8/5</sub> on Impact Toughness of P460NL1 Steel Welded Joints
作者: Simon A. SedmakMihajlo AranđelovićRadomir JovicicDorin RaduIvica Čamagić
作者单位: 1University of Belgrade
2Transilvania University of Brasov
刊名: Advanced Materials Research, 2020, Vol.5968 , pp.154-160
来源数据库: Trans Tech Journal
DOI: 10.4028/
关键词: Impact ToughnessWelded JointSteel P460NL1Cooling Time t8/5
原始语种摘要: The results of impact testing of welded joint specimens taken from a welded plate made of P460NL1 steel are presented in this paper, and analysed with regards to the cooling time t8/5, that was previously calculated. The aim was to determine how the cooling times that were measured, some of which were below the minimum required values, affected the toughness, in terms of total impact energy and its components, crack initiation and crack propagation energy. In addition, this analysis included the effects of temperatures measured at the opposite ends of the plate during the welding process, since this had also affected the cooling times for each welding pass. After observing the differences in total, crack initiation and propagation energy between the tested specimens taken from...
全文获取路径: PDF下载  Trans Tech 